GE Engineering plastics Physical properties directory >> LEXAN™ PC >> EXL1330 Physical property table

[下载EXL1330物性表PDF] Consult EXL1330

Lexan PC EXL1330 Physical property

-60℃延展性,中等流动速率,UV稳定,不透明色.优异的加工性能,应用广.

Property

TYPICAL PROPERTIES ⁽¹⁾
MECHANICAL	Value	Unit	Standard
Tensile Stress, yld, Type I, 50 mm/min	590	kgf/cm2	ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min	620	kgf/cm2	ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min	6	%	ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min	130	%	ASTM D 638
Tensile Modulus, 50 mm/min	21400	kgf/cm2	ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span	900	kgf/cm2	ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span	21000	kgf/cm2	ASTM D 790
Tensile Stress, yield, 50 mm/min	55	MPa	ISO 527
Tensile Stress, break, 50 mm/min	56	MPa	ISO 527
Tensile Strain, yield, 50 mm/min	5	%	ISO 527
Tensile Strain, break, 50 mm/min	>100	%	ISO 527
Tensile Modulus, 1 mm/min	2100	MPa	ISO 527
Flexural Stress, yield, 2 mm/min	85	MPa	ISO 178
Flexural Modulus, 2 mm/min	2100	MPa	ISO 178
Hardness, H358/30	90	MPa	ISO 2039-1
IMPACT	Value	Unit	Standard
Izod Impact, notched, 23°C	81	cm-kgf/cm	ASTM D 256
Izod Impact, notched, -30°C	69	cm-kgf/cm	ASTM D 256
Izod Impact, notched, -50°C	59	cm-kgf/cm	ASTM D 256
Izod Impact, notched, 23°C, 6.4mm	65	cm-kgf/cm	ASTM D 256
Izod Impact, double-gated, 23°C	108	cm-kgf/cm	SABIC Method
Instrumented Impact Total Energy, 23°C	539	cm-kgf	ASTM D 3763
Izod Impact, unnotched 80103 +23°C	NB	kJ/m2	ISO 180/1U
Izod Impact, unnotched 80103 -30°C	NB	kJ/m2	ISO 180/1U
Izod Impact, notched 80103 +23°C	70	kJ/m2	ISO 180/1A
Izod Impact, notched 80103 -30°C	55	kJ/m2	ISO 180/1A
Charpy 23°C, V-notch Edgew 80103 sp=62mm	75	kJ/m2	ISO 179/1eA
Charpy -30°C, V-notch Edgew 80103 sp=62mm	60	kJ/m2	ISO 179/1eA
Charpy 23°C, Unnotch Edgew 80103 sp=62mm	NB	kJ/m2	ISO 179/1eU
Charpy -30°C, Unnotch Edgew 80103 sp=62mm	NB	kJ/m2	ISO 179/1eU
THERMAL	Value	Unit	Standard
Vicat Softening Temp, Rate B/50	143	°C	ASTM D 1525
HDT, 0.45 MPa, 3.2 mm, unannealed	134	°C	ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed	120	°C	ASTM D 648
HDT, 1.82 MPa, 6.4 mm, unannealed	124	°C	ASTM D 648
CTE, -40°C to 40°C, flow	6.66E-05	1/°C	ASTM E 831
CTE, -40°C to 40°C, xflow	6.66E-05	1/°C	ASTM E 831
CTE, 23°C to 80°C, flow	7.2E-05	1/°C	ISO 11359-2
CTE, 23°C to 80°C, xflow	7.2E-05	1/°C	ISO 11359-2
Ball Pressure Test, 125°C +/- 2°C	PASSES	-	IEC 60695-10-2
Vicat Softening Temp, Rate B/50	143	°C	ISO 306
Vicat Softening Temp, Rate B/120	145	°C	ISO 306
HDT/Be, 0.45MPa Edgew 120104 sp=100mm	136	°C	ISO 75/Be
HDT/Ae, 1.8 MPa Edgew 120104 sp=100mm	125	°C	ISO 75/Ae
Relative Temp Index, Elec	125	°C	UL 746B
Relative Temp Index, Mech w/impact	115	°C	UL 746B
Relative Temp Index, Mech w/o impact	120	°C	UL 746B
PHYSICAL	Value	Unit	Standard
Specific Gravity	1.18	-	ASTM D 792
Mold Shrinkage, flow, 3.2 mm	0.4 - 0.8	%	SABIC Method
Mold Shrinkage, xflow, 3.2 mm	0.4 - 0.8	%	SABIC Method
Melt Flow Rate, 300°C/1.2 kgf	10	g/10 min	ASTM D 1238
Density	1.18	g/cm2	ISO 1183
Water Absorption, (23°C/sat)	0.35	%	ISO 62
Moisture Absorption (23°C / 50% RH)	0.15	%	ISO 62
Melt Volume Rate, MVR at 300°C/1.2 kg	9	cm210 min	ISO 1133
FLAME CHARACTERISTICS	Value	Unit	Standard
UL Recognized, 94HB Flame Class Rating (3)	0.8	mm	UL 94
Glow Wire Flammability Index 850°C, passes at	0.8	mm	IEC 60695-2-12
Glow Wire Flammability Index 960°C, passes at	1	mm	IEC 60695-2-12
Glow Wire Ignitability Temperature, 1.0 mm	875	°C	IEC 60695-2-13
Glow Wire Ignitability Temperature, 3.0 mm	875	°C	IEC 60695-2-13
Oxygen Index (LOI)	35	%	ISO 4589

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	120	°C
Drying Time	3 - 4	hrs
Drying Time (Cumulative)	48	hrs
Maximum Moisture Content	0.02	%
Melt Temperature	295 - 315	°C
Nozzle Temperature	290 - 310	°C
Front - Zone 3 Temperature	295 - 315	°C
Middle - Zone 2 Temperature	280 - 305	°C
Rear - Zone 1 Temperature	215 - 295	°C
Mold Temperature	70 - 95	°C
Back Pressure	0.3 - 0.7	MPa
Screw Speed	40 - 70	rpm
Shot to Cylinder Size	40 - 60	%
Vent Depth	0.025 - 0.076	mm

Parameter
Sheet Extrusion	Value	Unit
Drying Temperature	110 - 120	°C
Drying Time	3 - 4	hrs
Drying Time (Cumulative)	48	hrs
Maximum Moisture Content	0.02	%
Melt Temperature	245 - 260	°C
Barrel - Zone 1 Temperature	250 - 290	°C
Barrel - Zone 2 Temperature	245 - 270	°C
Barrel - Zone 3 Temperature	225 - 255	°C
Adapter Temperature	225 - 255	°C
Die Temperature	240 - 260	°C
Roll Stack Temp - Top	75 - 115	°C
Roll Stack Temp - Middle	80 - 125	°C
Roll Stack Temp - Bottom	120 - 145	°C

[下载EXL1330物性表PDF] Consult EXL1330

Physical properties of related products: 1173X BX9349 EX7631T EXL9330 EXL9132 EXL9134 EXL9335 EXL1414 EXL4419 EXL1414H EXL1132 ML7667 EXL1413T ML6413 ML6411 ML6412 EXL1494T EXL1463T EXL1433T EXL1414T EXL1443T EXL1434T EXL1434 EXL6414 EXL9112 EXL5689 EXL1162T EXL1132T EXL1810T EXL4016H EXL1192C EXL8414 EXL1483T EXL1484T EXL1036 EXL1493T EXL1182T EXL1890T EXL1112T EXL1112 EXL8134 EXL8454 EXL8483 EXL9330S EX1632T

Correlation search: EXL1330-111 EXL1330-701 EXL1330-BK1066 EXL1330-NA Lexan EXL1330 EXL1330物性 Sabic EXL1330 GE EXL1330 PC EXL1330 PC 工程塑料聚碳酸酯 PC 塑料 PC 物性

广州华秀塑胶有限公司不仅是专业的Lexan PC EXL1330原料供应商，亦注重技术支持及全方位的解决方案，提供从材料鉴定、模具设计、成型加工等系列帮助，亦可为客户量身定制各特殊性能之Lexan PC EXL1330材料，进而协助客户提高产品竟争力。

联络我们

地址:广州市天河区中山大道中439号东圃天银商贸大厦1720-1723室

电话:020-82582555

传真:020-82523699

Email: sales@va-so.cn

Lexan PC EXL1330报价 >>

常规产品

长纤增强尼龙66 长纤增强PPA
长纤增强尼龙6 长纤增强PP
长纤增强复合材料冲击改性复合尼龙66
冲击改性复合尼龙6 高强尼龙
冲击改性复合尼龙冲击改性复合材料
改性PP 改性的合金料
高温改性塑料含氟聚合物
改性POM 改性PBT
改性PC 焊接用复合塑料
高比重复合塑料永久防静电塑料
永久防静电ABS 永久防静电合金
永久防静电POM 其他导电材料
导电尼龙导电PE,导电PP
高温导电塑料导电POM
导电PBT 导电PC
其他非PTFE自润滑塑料非PTFE自润滑PA
非PTFE自润滑聚苯醚非PTFE自润滑PPA
非PTFE自润滑聚甲醛非PTFE自润滑聚碳酸酯
其他润滑塑料润滑尼龙
润滑烯烃润滑PPO(PPE+PS)
耐热润滑塑料润滑POM
润滑PBT 润滑弹性体
润滑PC 挤出PBT
热传导复合塑料其他PC
EMI/RFI屏蔽复合塑料预着色非填充树脂