GE Engineering plastics Physical properties directory >> LEXAN™ PC >> EXL1434 Physical property table

[下载EXL1434物性表PDF] Consult EXL1434

Lexan PC EXL1434 Physical property

-40℃延展性,UV稳定,中等流动速率.

Property

TYPICAL PROPERTIES ⁽¹⁾
MECHANICAL	Value	Unit	Standard
Tensile Stress, yld, Type I, 50 mm/min	560	kgf/cm2	ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min	510	kgf/cm2	ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min	6	%	ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min	98	%	ASTM D 638
Tensile Modulus, 50 mm/min	20500	kgf/cm2	ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span	940	kgf/cm2	ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span	22700	kgf/cm2	ASTM D 790
Hardness, Rockwell L	89	-	ASTM D 785
Hardness, Rockwell R	121	-	ASTM D 785
Tensile Stress, yield, 50 mm/min	57	MPa	ISO 527
Tensile Stress, break, 50 mm/min	60	MPa	ISO 527
Tensile Strain, yield, 50 mm/min	6	%	ISO 527
Tensile Strain, break, 50 mm/min	120	%	ISO 527
Tensile Modulus, 1 mm/min	2150	MPa	ISO 527
Flexural Stress, yield, 2 mm/min	85	MPa	ISO 178
Flexural Modulus, 2 mm/min	2250	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, notched, 23°C	88	cm-kgf/cm	ASTM D 256
Izod Impact, notched, -30°C	78	cm-kgf/cm	ASTM D 256
Instrumented Impact Total Energy, 23°C	714	cm-kgf	ASTM D 3763
Izod Impact, unnotched 80103 +23°C	NB	kJ/m2	ISO 180/1U
Izod Impact, unnotched 80103 -30°C	NB	kJ/m2	ISO 180/1U
Izod Impact, notched 80103 +23°C	70	kJ/m2	ISO 180/1A
Izod Impact, notched 80103 -30°C	60	kJ/m2	ISO 180/1A
Charpy 23°C, V-notch Edgew 80103 sp=62mm	70	kJ/m2	ISO 179/1eA
Charpy -30°C, V-notch Edgew 80103 sp=62mm	65	kJ/m2	ISO 179/1eA
Charpy 23°C, Unnotch Edgew 80103 sp=62mm	NB	kJ/m2	ISO 179/1eU
Charpy -30°C, Unnotch Edgew 80103 sp=62mm	NB	kJ/m2	ISO 179/1eU
THERMAL	Value	Unit	Standard
Vicat Softening Temp, Rate B/50	145	°C	ASTM D 1525
HDT, 0.45 MPa, 3.2 mm, unannealed	139	°C	ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed	124	°C	ASTM D 648
CTE, -40°C to 40°C, flow	6.97E-05	1/°C	ASTM E 831
CTE, -40°C to 40°C, xflow	7.47E-05	1/°C	ASTM E 831
CTE, 23°C to 80°C, flow	7.2E-05	1/°C	ISO 11359-2
CTE, 23°C to 80°C, xflow	7.2E-05	1/°C	ISO 11359-2
Ball Pressure Test, 125°C +/- 2°C	Passes	-	IEC 60695-10-2
Vicat Softening Temp, Rate B/50	145	°C	ISO 306
Vicat Softening Temp, Rate B/120	146	°C	ISO 306
HDT/Be, 0.45MPa Edgew 120104 sp=100mm	140	°C	ISO 75/Be
HDT/Ae, 1.8 MPa Edgew 120104 sp=100mm	128	°C	ISO 75/Ae
Relative Temp Index, Elec	130	°C	UL 746B
Relative Temp Index, Mech w/impact	120	°C	UL 746B
Relative Temp Index, Mech w/o impact	125	°C	UL 746B
PHYSICAL	Value	Unit	Standard
Specific Gravity	1.18	-	ASTM D 792
Mold Shrinkage, flow, 3.2 mm	0.4 - 0.8	%	SABIC Method
Mold Shrinkage, xflow, 3.2 mm	0.4 - 0.8	%	SABIC Method
Melt Flow Rate, 300°C/1.2 kgf	10	g/10 min	ASTM D 1238
Density	1.19	g/cm2	ISO 1183
Water Absorption, (23°C/sat)	0.35	%	ISO 62
Moisture Absorption (23°C / 50% RH)	0.15	%	ISO 62
Melt Volume Rate, MVR at 300°C/1.2 kg	9	cm210 min	ISO 1133
ELECTRICAL	Value	Unit	Standard
Volume Resistivity	>1.E+15	Ohm-cm	ASTM D 257
Surface Resistivity	>1.E+15	Ohm	ASTM D 257
Dielectric Strength, in oil, 0.8 mm	16.2	kV/mm	ASTM D 149
Relative Permittivity, 100 Hz	2.68	-	ASTM D 150
Relative Permittivity, 1 MHz	2.64	-	ASTM D 150
Dissipation Factor, 100 Hz	0.0012	-	ASTM D 150
Dissipation Factor, 1 MHz	0.0093	-	ASTM D 150
FLAME CHARACTERISTICS	Value	Unit	Standard
Glow Wire Flammability Index 850°C, passes at	0.8	mm	IEC 60695-2-12
Glow Wire Flammability Index 960°C, passes at	1	mm	IEC 60695-2-12
Glow Wire Ignitability Temperature, 1.0 mm	875	°C	IEC 60695-2-13
Glow Wire Ignitability Temperature, 3.0 mm	875	°C	IEC 60695-2-13
Oxygen Index (LOI)	37	%	ISO 4589

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	120	°C
Drying Time	3 - 4	hrs
Drying Time (Cumulative)	48	hrs
Maximum Moisture Content	0.02	%
Melt Temperature	295 - 315	°C
Nozzle Temperature	290 - 310	°C
Front - Zone 3 Temperature	295 - 315	°C
Middle - Zone 2 Temperature	280 - 305	°C
Rear - Zone 1 Temperature	215 - 295	°C
Mold Temperature	70 - 95	°C
Back Pressure	0.3 - 0.7	MPa
Screw Speed	40 - 70	rpm
Shot to Cylinder Size	40 - 60	%
Vent Depth	0.025 - 0.076	mm

[下载EXL1434物性表PDF] Consult EXL1434

Physical properties of related products: EXL9330S EXL8483 EX1632T 1173X BX9349 EX7631T EXL1330 EXL9330 EXL9132 EXL9134 EXL9335 EXL1414 EXL4419 EXL1414H EXL1132 ML7667 EXL1413T ML6413 ML6411 ML6412 EXL1494T EXL1463T EXL1433T EXL1414T EXL1443T EXL1434T EXL6414 EXL9112 EXL5689 EXL1162T EXL1132T EXL1810T EXL4016H EXL1192C EXL8414 EXL1483T EXL1484T EXL1036 EXL1493T EXL1182T EXL1890T EXL1112T EXL1112 EXL8134 EXL8454

Correlation search: EXL1434-111 EXL1434-701 EXL1434-BK1066 EXL1434-NA Lexan EXL1434 EXL1434物性 Sabic EXL1434 GE EXL1434 PC EXL1434 聚碳酸酯 PC 塑胶原料 PC 树脂 GE PC

广州华秀塑胶有限公司不仅是专业的Lexan PC EXL1434原料供应商，亦注重技术支持及全方位的解决方案，提供从材料鉴定、模具设计、成型加工等系列帮助，亦可为客户量身定制各特殊性能之Lexan PC EXL1434材料，进而协助客户提高产品竟争力。

联络我们

地址:广州市天河区中山大道中439号东圃天银商贸大厦1720-1723室

电话:020-82582555

传真:020-82523699

Email: sales@va-so.cn

Lexan PC EXL1434报价 >>

常规产品

长纤增强尼龙66 长纤增强PPA
长纤增强尼龙6 长纤增强PP
长纤增强复合材料冲击改性复合尼龙66
冲击改性复合尼龙6 高强尼龙
冲击改性复合尼龙冲击改性复合材料
改性PP 改性的合金料
高温改性塑料含氟聚合物
改性POM 改性PBT
改性PC 焊接用复合塑料
高比重复合塑料永久防静电塑料
永久防静电ABS 永久防静电合金
永久防静电POM 其他导电材料
导电尼龙导电PE,导电PP
高温导电塑料导电POM
导电PBT 导电PC
其他非PTFE自润滑塑料非PTFE自润滑PA
非PTFE自润滑聚苯醚非PTFE自润滑PPA
非PTFE自润滑聚甲醛非PTFE自润滑聚碳酸酯
其他润滑塑料润滑尼龙
润滑烯烃润滑PPO(PPE+PS)
耐热润滑塑料润滑POM
润滑PBT 润滑弹性体
润滑PC 挤出PBT
热传导复合塑料其他PC
EMI/RFI屏蔽复合塑料预着色非填充树脂